The PVA roller is crafted from specialized urethane resin as raw material. It is widely applicable to high-precision and high-quality production environments, specifically for printed circuit boards and lead frame plate production where high-performance water absorption is essential.
Core Usages:
| Parameter | Specification | Parameter | Specification |
|---|---|---|---|
| Method | Molecular Hole / Substitution | Hole Shape | Honeycomb continuous |
| Porosity | 90-92% | Avg. Hole Size | 60-130-300 nm |
| Apparent Density | 0.068-0.088 g/cm³ | 35% Pressures | 24-34 g/cm² |
| Tensile Strength | 3.1 kg/cm² | Temp Range | 0-65ºC |
| Tensile Extension | 220-230% | Melting Point | 180ºC |
| Anti-wear | 20,000-50,000 times | Water Absorption | 10-150 times material weight |
| Absorption Rate | 2-15 cm/sec | Hardness | Soft (Wet) / Hard (Dry) |
| Dimensions | Customized Diameter and Length | ||
The rollers are made from a high-quality specialized urethane resin, resulting in a PVA (Polyvinyl Alcohol) structure that offers exceptional absorption properties.
These PVA sponge rollers are highly efficient, capable of absorbing water ranging from 10 to 150 times their own material weight.
Yes, we provide fully customized solutions. Both the diameter and the length of the roller can be adjusted to meet your specific industrial requirements.
The recommended operating temperature range is between 0ºC and 65ºC. The material has a melting point of approximately 180ºC.
The roller is designed to be soft and pliable when in a wet condition, which is ideal for cleaning and dehydration without scratching surfaces. It becomes hard when completely dry.
The product features weak acid and base resistance, making it suitable for various industrial cleaning processes involving mild chemical solutions.